Preparation of AC/TiO2 Composites from Activated Carbon Modified by HNO3 and Their Photocatalytic Activity
* 본 문서는 배포용으로 복사 및 편집이 불가합니다.
서지정보
ㆍ발행기관 : 한국탄소학회
ㆍ수록지정보 : Carbon Letters / 8권 / 2호
ㆍ저자명 : Ming-Liang Chen, Won-Chun Oh
ㆍ저자명 : Ming-Liang Chen, Won-Chun Oh
목차
1. Introduction2. Experimental
3. Results and Discussion
4. Conclusions
References
한국어 초록
In this work, activated carbon (AC) after HNO3 modification was used as the support during the production of supported TiO2 to increase the high deposition efficiency and the photocatalytic activity. The results of N2 adsorption showed that the BET surface area of samples decreased with an increasing of the concentration of HNO3 due to the penetration of TiO2. From XRD data, a single crystal structure of anatase peak was observed in diffraction patterns for the AC coated with titanium complexes. From the SEM results, almost all particles were aggregated with each other at the carbon surface and AC was covered with TiO2 particles in all of the samples. The EDX spectra show the presence of C, O, Ti and other elements. It was also observed a decreasing of amount of C content with increasing Ti and O content from the EDX. The results of FT-IR revealed that the modified AC contained moresurface oxygen bearing groups than that of the original AC. The effect of surface acidity and basity calculated from Boehm titration method was also evaluated from correlations as a function of NaOH, NaHCO3, and Na2CO3 uptake. The surface modification of AC by HNO3 leads to an increase in the catalytic efficiency of AC/TiO2 catalysts, and the catalytic efficiency increases with increasing of HNO3 concentration.
Keywords : Activated carbon, TiO2, SEM, XRD, EDX, FT-IR, Boehm titration, Photocatalytic activity
영어 초록
In this work, activated carbon (AC) after HNO3 modification was used as the support during the production of supported TiO2 to increase the high deposition efficiency and the photocatalytic activity. The results of N2 adsorption showed that the BET surface area of samples decreased with an increasing of the concentration of HNO3 due to the penetration of TiO2. From XRD data, a single crystal structure of anatase peak was observed in diffraction patterns for the AC coated with titanium complexes. From the SEM results, almost all particles were aggregated with each other at the carbon surface and AC was covered with TiO2 particles in all of the samples. The EDX spectra show the presence of C, O, Ti and other elements. It was also observed a decreasing of amount of C content with increasing Ti and O content from the EDX. The results of FT-IR revealed that the modified AC contained more surface oxygen bearing groups than that of the original AC. The effect of surface acidity and basity calculated from Boehm titration method was also evaluated from correlations as a function of NaOH, NaHCO3, and Na2CO3 uptake. The surface modification of AC by HNO3 leads to an increase in the catalytic efficiency of AC/TiO2 catalysts, and the catalytic efficiency increases with increasing of HNO3 concentration.Keywords : Activated carbon, TiO2, SEM, XRD, EDX, FT-IR, Boehm titration, Photocatalytic activity참고 자료
없음"Carbon Letters"의 다른 논문
Electrochemical Behaviors of Activated Carbons Prepared..3페이지
X-ray Photoelectron Spectroscopy Study of Cobalt Suppor..7페이지
Properties of Carbon Black/SBR Rubber Composites Filled..5페이지
Removal of Pesticide (Endosulphan) from Water via Adsor..7페이지
X-ray Diffraction Patterns of Activated Carbons Prepare..6페이지