Properties of Carbon Black/SBR Rubber Composites Filled by Surface Modified Carbon Blacks
* 본 문서는 배포용으로 복사 및 편집이 불가합니다.
서지정보
ㆍ발행기관 : 한국탄소학회
ㆍ수록지정보 : Carbon Letters / 8권 / 2호
ㆍ저자명 : Shuang-Ye Dai, Ge-You Ao, Myung-Soo Kim
ㆍ저자명 : Shuang-Ye Dai, Ge-You Ao, Myung-Soo Kim
목차
1. Introduction2. Experimental
3. Results and Discussion
4. Conclusions
References
한국어 초록
Properties of carbon blacks and carbon black/SBR rubber composites filled by surface modified carbon blacks were examined. Although the specific surface area of carbon blacks increased after the surface modifications with heat, acid, and base, there were no obvious changes in resistivity. The composites filled by heat treated carbon blacks showed a higher tensile strength and elongation than those filled by raw blacks. The acid and base treated carbon blacks filled composites also showed higher tensile strength but similar elongation values with those filled by raw blacks. With increasing loading ratio, both tensile strength and elongation increased, and appeared a maximum value at 30-40 phr. Modulus at 300% strain remained increasing with further loading of carbon blacks. At the same loading, the heat treated black filled composites showed similar modulus values with composites filled by raw blacks but for base and acid treated black filled composites much higher values were obtained. After the surface modification, the functional groups which played an important role in reinforcement action were changed.Keywords : Carbon black, Surface modification, Rubber reinforcement, Mechanical properties
영어 초록
Properties of carbon blacks and carbon black/SBR rubber composites filled by surface modified carbon blacks were examined. Although the specific surface area of carbon blacks increased after the surface modifications with heat, acid, and base, there were no obvious changes in resistivity. The composites filled by heat treated carbon blacks showed a higher tensile strength and elongation than those filled by raw blacks. The acid and base treated carbon blacks filled composites also showed higher tensile strength but similar elongation values with those filled by raw blacks. With increasing loading ratio, both tensile strength and elongation increased, and appeared a maximum value at 30-40 phr. Modulus at 300% strain remained increasing with further loading of carbon blacks. At the same loading, the heat treated black filled composites showed similar modulus values with composites filled by raw blacks but for base and acid treated black filled composites much higher values were obtained. After the surface modification, the functional groups which played an important role in reinforcement action were changed.Keywords : Carbon black, Surface modification, Rubber reinforcement, Mechanical properties참고 자료
없음"Carbon Letters"의 다른 논문
Electrochemical Behaviors of Activated Carbons Prepared..3페이지
X-ray Photoelectron Spectroscopy Study of Cobalt Suppor..7페이지
Preparation of AC/TiO2 Composites from Activated Carbon..7페이지
Removal of Pesticide (Endosulphan) from Water via Adsor..7페이지
X-ray Diffraction Patterns of Activated Carbons Prepare..6페이지