Preparation and Characterization of Pitch/Cokes Composite Anode Material for High Power Lithium Secondary Battery
* 본 문서는 배포용으로 복사 및 편집이 불가합니다.
서지정보
ㆍ발행기관 : 한국탄소학회
ㆍ수록지정보 : Carbon Letters / 9권 / 3호
ㆍ저자명 : Lan Yu, Kijung Kim, Daeyong Park, Myung-Soo Kim, Kab-Il Kim and
ㆍ저자명 : Lan Yu, Kijung Kim, Daeyong Park, Myung-Soo Kim, Kab-Il Kim and
목차
1. 서 론2. 실험 방법
3. 결과 및 토의
4. 결 론
참고문헌
한국어 초록
Petroleum pitch and coke with wet mixture method or with dry mixture method were investigated to develop the composite anodic carbon material of high power lithium ion battery. Cokes coated with pitch were obtained by the heat treatment of mixture of cokes and pitch with different weight ratios at 800 ~ 1200oC. The charge and discharge characteristic of the consequent composite anodic carbon material assembled in batteries was tested. Cokes with wet mixture method have a smooth surface and their capacity changed little with changing temperature and content as compared to the cokes with dry mixture method. Although the reversible capacities showed different values by the anode manufacturing method, the composite anode with the mixture of 20 wt% of petroleum pitch and 80 wt% of coke showed the higher power capability and initial efficiency than the pitch based anode. However, the reversible capacity of the composite anode showed the reduced value as compared with the pitch based anode.Keywords : Lithium Secondary Battery, Anode, Carbon, Cokes, Pitch
영어 초록
Petroleum pitch and coke with wet mixture method or with dry mixture method were investigated to develop the composite anodic carbon material of high power lithium ion battery. Cokes coated with pitch were obtained by the heat treatment of mixture of cokes and pitch with different weight ratios at 800 ~ 1200oC. The charge and discharge characteristic of the consequent composite anodic carbon material assembled in batteries was tested. Cokes with wet mixture method have a smooth surface and their capacity changed little with changing temperature and content as compared to the cokes with dry mixture method. Although the reversible capacities showed different values by the anode manufacturing method, the composite anode with the mixture of 20 wt% of petroleum pitch and 80 wt% of coke showed the higher power capability and initial efficiency than the pitch based anode. However, the reversible capacity of the composite anode showed the reduced value as compared with the pitch based anode.Keywords : Lithium Secondary Battery, Anode, Carbon, Cokes, Pitch참고 자료
없음"Carbon Letters"의 다른 논문
Steam Activated Carbon Preparation Using HTFBR from Bio..7페이지
Improvement of Thermal Stability of Electrospun PAN Fib..3페이지
Improved Photo Degradation of Rhodamine B Dye using Iro..5페이지
Development of Supercapacitors Using Porous Carbon Mate..7페이지
Kinetic Modeling for Biosorption of Metylene Blue onto ..7페이지