Improvement of the Field Emission Stability of Carbon Nanotube Paste Emitter by Post-treatments
* 본 문서는 배포용으로 복사 및 편집이 불가합니다.
서지정보
ㆍ발행기관 : 한국탄소학회
ㆍ수록지정보 : Carbon Letters / 10권 / 3호
ㆍ저자명 : Young Chul Choi, Mun Seok Jeong
ㆍ저자명 : Young Chul Choi, Mun Seok Jeong
목차
1. Introduction2. Experimental
3. Results and Discussion
4. Conclusions
References
한국어 초록
The field emitters were fabricated by screen-printing of carbon nanotube paste, and their emission stabilities were evaluated. It was found that the emission stability measured in a sealed device is much higher than that measured in a vacuum chamber in spite of similar pressure. This was because oxygen gas was scarcely remained in the sealed device, while the gas is continuously supplied into the vacuum chamber during the stability measurement. It was found that the plasma treatment etched the protruded CNTs, resulting in the uniform height of CNT tips. As a result, the stability was increased remarkably. It was also found that the stability of CNT paste emitter was improved by electrical aging and that the optimum condition for the aging was varied with the size of emitter.영어 초록
The field emitters were fabricated by screen-printing of carbon nanotube paste, and their emission stabilities were evaluated. It was found that the emission stability measured in a sealed device is much higher than that measured in a vacuum chamber in spite of similar pressure. This was because oxygen gas was scarcely remained in the sealed device, while the gas is continuously supplied into the vacuum chamber during the stability measurement. It was found that the plasma treatment etched the protruded CNTs, resulting in the uniform height of CNT tips. As a result, the stability was increased remarkably. It was also found that the stability of CNT paste emitter was improved by electrical aging and that the optimum condition for the aging was varied with the size of emitter.참고 자료
없음"Carbon Letters"의 다른 논문
Nuclear Graphites (I) : Oxidation Behaviors11페이지
Low Temperature Growth of High-Quality Carbon Nanotubes..4페이지
Thermal Emissivity of Nuclear Graphite as a Function of..5페이지
CO2 Adsorption of Amine Functionalized Activated Carbon..4페이지
Hydrogen Adsorption of PAN-based Porous Carbon Nanofibe..4페이지
Preparation and Electroactivities of Carbon Nanotubes-s..4페이지
Effect of pH-dependent Solubility on Release Behavior o..5페이지
Relationship Between Exothermic Heat and Carbon Content..6페이지
Thermostable Adsorption Filter Immobilized with Super A..4페이지
Amino Silane, Vinyl Silane, TESPD, ZS (TESPD/Zinc Compl..8페이지