Tensile Properties and Morphology of Carbon Fibers Stabilized by Plasma Treatment
* 본 문서는 배포용으로 복사 및 편집이 불가합니다.
서지정보
ㆍ발행기관 : 한국탄소학회
ㆍ수록지정보 : Carbon Letters / 12권 / 1호
ㆍ저자명 : 이승욱, 이화영, 장성연, 조승무, 이훈수, 이성호
ㆍ저자명 : 이승욱, 이화영, 장성연, 조승무, 이훈수, 이성호
목차
1. Introduction2. Experimental
3. Results and Discussion
4. Conclusions
References
한국어 초록
Commercial PAN fibers were thermally stabilized at 220 or 240oC for 30 min. Those fibers were further stabilized using radio-frequency (RF) capacitive plasma discharge during 5 or 15 min. From Fourier transform infrared spectroscopy results, it was observed that an additional plasma treatment led to further stabilization of PAN fibers. After stabilization, carbonization was performed to investigate the final tensile properties of the fabricated carbon fibers (CFs). The results revealed that a combination of thermal and plasma treatment is a possible stabilization process for manufacturing CFs. Morphology of CFs was investigated using scanning electron microscopy. The morphology shows that the plasma stabilization performed by the RF large gap plasma discharge may damage the surface of the CF, so it is necessary to select a proper process condition to minimize the damage.Keywords : Polyacrylonitrile, Carbon fiber, Plasma treatment, Tensile properties, Scanning electron microscopy
영어 초록
Commercial PAN fibers were thermally stabilized at 220 or 240oC for 30 min. Those fibers were further stabilized using radio-frequency (RF) capacitive plasma discharge during 5 or 15 min. From Fourier transform infrared spectroscopy results, it was observed that an additional plasma treatment led to further stabilization of PAN fibers. After stabilization, carbonization was performed to investigate the final tensile properties of the fabricated carbon fibers (CFs). The results revealed that a combination of thermal and plasma treatment is a possible stabilization process for manufacturing CFs. Morphology of CFs was investigated using scanning electron microscopy. The morphology shows that the plasma stabilization performed by the RF large gap plasma discharge may damage the surface of the CF, so it is necessary to select a proper process condition to minimize the damage.Keywords : Polyacrylonitrile, Carbon fiber, Plasma treatment, Tensile properties, Scanning electron microscopy참고 자료
없음"Carbon Letters"의 다른 논문
Thermal Insulation Properties of Epoxy/Mesoporous Carbo..4페이지
Preparation and Characteristics of Conducting Polymer-C..5페이지
Preparation of Activated Carbon Fibers from Cost Effect..4페이지
Hydrogen Storage by Carbon Fibers Synthesized by Pyroly..5페이지
Polymerization and Thermal Characteristics of Acrylonit..8페이지