Polymerization and Thermal Characteristics of Acrylonitrile/Dicyclohexy lammonium2-Cyanoacrylate Copolymers for Carbon Fiber Precursors
* 본 문서는 배포용으로 복사 및 편집이 불가합니다.
서지정보
ㆍ발행기관 : 한국탄소학회
ㆍ수록지정보 : Carbon Letters / 12권 / 1호
ㆍ저자명 : 김기영, 박우리, 정영식, 신동근, 한진욱
ㆍ저자명 : 김기영, 박우리, 정영식, 신동근, 한진욱
목차
1. Introduction2. Experimental
3. Results and Discussion
4. Conclusions
References
한국어 초록
This study experimentally investigated dicyclohexylammonium 2-cyanoacrylate (CA) as a potential comonomer for polyacrylonitrile (PAN) based carbon fiber precursors. The P(AN-CA) copolymers with different CA contents (0.19-0.78 mol% in the feed) were polymerized using solution polymerization with 2,2-azobis(isobutyronitrile) as an initiator. The chemical structure and composition of P(AN-CA) copolymers were determined by proton nuclear magnetic resonance and elemental analysis, an the copolymer composition was similar to the feeding ratio of the monomers. The effects of CA comonomer on the thermal properties of its copolymers were characterized differential scanning calorimetry (DSC) in nitrogen and air atmospheres. The DSC curves of P(AN-CA) under nitrogen atmosphere indicated that the initiation temperature for cyclization of nitrile groups was reduced to around 235oC. The heat release and the activation energy for cyclization reactions were decreased in comparison with those of PAN homopolymers. On the other hand, under air atmosphere, the P(AN-CA) with 0.78 mol% CA content showed that the initiation temperature of cyclization was significantly lowered to 160.1oC. The activation energy value showed 116 kJ/mol, that was smaller than that of the copolymers with 0.82 mol% of itaconic acids. The thermal stability of P(AN-CA), evidenced by thermogravimetric analyses in air atmosphere, was found higher than PAN homopolymer and similar to P(AN-IA) copolymers. Therefore, this study successfully demonstrated the great potential of P(AN-CA) copolymers as carbon fiber precursors, taking advantages of the temperature-lowering effects of CA comonomers and higher thermal stability of the CA copolymers for the stabilizing processes.Keywords : Dicyclohexylammonium 2-cyanoacrylate, Polyacrylonitrile copolymer, Carbon fiber precursor, Stabilization behavior
영어 초록
This study experimentally investigated dicyclohexylammonium 2-cyanoacrylate (CA) as a potential comonomer for polyacrylonitrile (PAN) based carbon fiber precursors. The P(AN-CA) copolymers with different CA contents (0.19-0.78 mol% in the feed) were polymerized using solution polymerization with 2,2-azobis(isobutyronitrile) as an initiator. The chemical structure and composition of P(AN-CA) copolymers were determined by proton nuclear magnetic resonance and elemental analysis, an the copolymer composition was similar to the feeding ratio of the monomers. The effects of CA comonomer on the thermal properties of its copolymers were characterized differential scanning calorimetry (DSC) in nitrogen and air atmospheres. The DSC curves of P(AN-CA) under nitrogen atmosphere indicated that the initiation temperature for cyclization of nitrile groups was reduced to around 235oC. The heat release and the activation energy for cyclization reactions were decreased in comparison with those of PAN homopolymers. On the other hand, under air atmosphere, the P(AN-CA) with 0.78 mol% CA content showed that the initiation temperature of cyclization was significantly lowered to 160.1oC. The activation energy value showed 116 kJ/mol, that was smaller than that of the copolymers with 0.82 mol% of itaconic acids. The thermal stability of P(AN-CA), evidenced by thermogravimetric analyses in air atmosphere, was found higher than PAN homopolymer and similar to P(AN-IA) copolymers. Therefore, this study successfully demonstrated the great potential of P(AN-CA) copolymers as carbon fiber precursors, taking advantages of the temperature-lowering effects of CA comonomers and higher thermal stability of the CA copolymers for the stabilizing processes.Keywords : Dicyclohexylammonium 2-cyanoacrylate, Polyacrylonitrile copolymer, Carbon fiber precursor, Stabilization behavior참고 자료
없음"Carbon Letters"의 다른 논문
Thermal Insulation Properties of Epoxy/Mesoporous Carbo..4페이지
Preparation and Characteristics of Conducting Polymer-C..5페이지
Preparation of Activated Carbon Fibers from Cost Effect..4페이지
Hydrogen Storage by Carbon Fibers Synthesized by Pyroly..5페이지
Effect of Process Condition on Tensile Properties of Ca..5페이지