Molecular structure effects of the pitches on preparation of activated carbon fibers from electrospinning
* 본 문서는 배포용으로 복사 및 편집이 불가합니다.
서지정보
ㆍ발행기관 : 한국탄소학회
ㆍ수록지정보 : Carbon Letters / 12권 / 2호
ㆍ저자명 : 김보혜, ArshadHussainWazir, 양갑승, 방윤혁, 김성령
ㆍ저자명 : 김보혜, ArshadHussainWazir, 양갑승, 방윤혁, 김성령
목차
1. Introduction2. Experimental
3. Results and Discussion
4. Conclusions
References
한국어 초록
Two pitches with different average molecular structures were electrospun and compared interms of the properties of their fibers after oxidative stabilization, carbonization, and activation.
The precursor with a higher molecular weight and greater content of aliphatic groups
(Pitch A) resulted in better solubility and spinnability compared to that with a lower molecular
weight and lower aliphatic group content (Pitch B). The electrical conductivity of the
carbon fiber web from Pitch A of 67 S/cm was higher than that from Pitch B of 52 S/cm. The
carbon fiber web based on Pitch A was activated more readily with lower activation energy,
resulting in a higher specific surface area compared to the carbon fiber based on Pitch B
(Pitch A, 2053 m2/g; Pitch B, 1374 m2/g).
Key words: pitch, electrospinning, carbon fiber, spinnability, molecular structure, activation
영어 초록
Two pitches with different average molecular structures were electrospun and compared interms of the properties of their fibers after oxidative stabilization, carbonization, and activation.The precursor with a higher molecular weight and greater content of aliphatic groups(Pitch A) resulted in better solubility and spinnability compared to that with a lower molecularweight and lower aliphatic group content (Pitch B). The electrical conductivity of thecarbon fiber web from Pitch A of 67 S/cm was higher than that from Pitch B of 52 S/cm. Thecarbon fiber web based on Pitch A was activated more readily with lower activation energy,resulting in a higher specific surface area compared to the carbon fiber based on Pitch B(Pitch A, 2053 m2/g; Pitch B, 1374 m2/g).Key words: pitch, electrospinning, carbon fiber, spinnability, molecular structure, activation참고 자료
없음"Carbon Letters"의 다른 논문
Application and evaluation of boron nitride-assisted li..4페이지
Influence of phosphoric acid treatment on hydrogen adso..4페이지
Effects of positive and negative stretching on the stru..5페이지
Parametric study on synthesis of carbon nanotubes by th..5페이지
Effects of heat-treatment temperature on carbon-based c..7페이지