Structural evolution and kinetic study of high isotacticity poly(acrylonitrile) during isothermal pre-oxidation
* 본 문서는 배포용으로 복사 및 편집이 불가합니다.
서지정보
ㆍ발행기관 : 한국탄소학회
ㆍ수록지정보 : Carbon Letters / 12권 / 4호
ㆍ저자명 : LiZhang, YongqiangDai, YiKaiandRi-guangJin
ㆍ저자명 : LiZhang, YongqiangDai, YiKaiandRi-guangJin
목차
1. Introduction2. Experiment
3. Characterization
4. Results and Discussion
5. Conclusions
References
한국어 초록
Isotactic polyacrylonitrile (PAN) with triad isotacticity of 0.53, which was determined by13C nuclear magnetic resonance, using dialkylmagnesium as an initiator, was successfully
synthesized. Isothermal treatment of iso-PAN was conducted in air at 200, 220, 250 and
280oC. Structural evolutions and chemical changes were studied with Fourier transformation
infrared and wide-angle X-ray diffraction during stabilization. A new parameter carbon
nanofiber = I2240cm
-1/ (I1595cm
-1+f*I1595cm
-1) was defined to evaluate residual nitrile groups.
Crystallinity and crystal size were calculated with X-ray diffraction dates. The results
indicated that the nitrile groups had partly converted into a ladder structure as stabilization
proceeded. The rate of reaction increased with treatment temperature; crystallinity and
crystal size decreased proportionally to pyrolysis temperature. The iso-conversional method
coupled with the Kissinger and Flynn-Wall-Ozawa methods were used to determine kinetic
parameters via differential scanning calorimetry analysis with different heating rates. The
active energy of the reaction was 171.1 and 169.1 kJ/mol, calculated with the two methods
respectively and implied the sensitivity of the reaction with temperature.
영어 초록
Isotactic polyacrylonitrile (PAN) with triad isotacticity of 0.53, which was determined by13C nuclear magnetic resonance, using dialkylmagnesium as an initiator, was successfullysynthesized. Isothermal treatment of iso-PAN was conducted in air at 200, 220, 250 and280oC. Structural evolutions and chemical changes were studied with Fourier transformationinfrared and wide-angle X-ray diffraction during stabilization. A new parameter carbonnanofiber = I2240cm-1/ (I1595cm-1+f*I1595cm-1) was defined to evaluate residual nitrile groups.Crystallinity and crystal size were calculated with X-ray diffraction dates. The resultsindicated that the nitrile groups had partly converted into a ladder structure as stabilizationproceeded. The rate of reaction increased with treatment temperature; crystallinity andcrystal size decreased proportionally to pyrolysis temperature. The iso-conversional methodcoupled with the Kissinger and Flynn-Wall-Ozawa methods were used to determine kineticparameters via differential scanning calorimetry analysis with different heating rates. Theactive energy of the reaction was 171.1 and 169.1 kJ/mol, calculated with the two methodsrespectively and implied the sensitivity of the reaction with temperature.참고 자료
없음태그
"Carbon Letters"의 다른 논문
Effect of crystallinity on the electrochemical properti..4페이지
Effects of oil absorption on the wear behaviors of carb..3페이지
Performance of modified graphite as anode material for ..6페이지
Influence of oxyfluorination on activated carbon nanofi..7페이지
Effect of additional heat-treatment temperature on chem..6페이지