Pore Structure Characterization of Poly(vinylidene chloride)-Derived Nanoporous Carbons
* 본 문서는 배포용으로 복사 및 편집이 불가합니다.
서지정보
ㆍ발행기관 : 한국탄소학회
ㆍ수록지정보 : Carbon Letters / 13권 / 4호
ㆍ저자명 : Hwan Jung Jung, Yong-Jung Kim, Dae Ho Lee, Jong Hun Han, Kap Seung Yang, Cheol-Min Yang
ㆍ저자명 : Hwan Jung Jung, Yong-Jung Kim, Dae Ho Lee, Jong Hun Han, Kap Seung Yang, Cheol-Min Yang
목차
Abstract1. Introduction
2. Experimental
3. Results and Discussion
4. Conclusions
Acknowledgements
References
한국어 초록
Poly(vinylidene chloride) (PVDC)-derived nanoporous carbons were prepared by various activation methods: heat-treatment under an inert atmosphere, steam activation, and potassium hydroxide (KOH) activation at 873, 1073, and 1273 K. The pore structures of PVDC-derived nanoporous carbons were characterized by the N<SUB>2</SUB> adsorption technique at 77 K. Heat treatment in an inert atmosphere increased the specific surface area and micropore volume with elevating temperature, while the average micropore width near 0.65 nm was not significantly changed, reflecting the characteristic pore structure of ultramicroporous carbon. Steam activation for PVDC at 873 and 1073 K also yielded ultramicroporosity. On the other hand, the steam activated sample at 1273 K had a wider average micropore width of 1.48 nm, correlating with a supermicropore. The KOH activation increased the micropore volume with elevating temperature, which is accompanied by enlargement of the average micropore width from 0.67 to 1.12 nm. The average pore widths of KOH-activated samples were strongly governed by the activation temperature. We expect that these approaches can be utilized to simply control the porosity of PVDC-derived nanoporous carbons.영어 초록
Poly(vinylidene chloride) (PVDC)-derived nanoporous carbons were prepared by various activation methods: heat-treatment under an inert atmosphere, steam activation, and potassium hydroxide (KOH) activation at 873, 1073, and 1273 K. The pore structures of PVDC-derived nanoporous carbons were characterized by the N<SUB>2</SUB> adsorption technique at 77 K. Heat treatment in an inert atmosphere increased the specific surface area and micropore volume with elevating temperature, while the average micropore width near 0.65 nm was not significantly changed, reflecting the characteristic pore structure of ultramicroporous carbon. Steam activation for PVDC at 873 and 1073 K also yielded ultramicroporosity. On the other hand, the steam activated sample at 1273 K had a wider average micropore width of 1.48 nm, correlating with a supermicropore. The KOH activation increased the micropore volume with elevating temperature, which is accompanied by enlargement of the average micropore width from 0.67 to 1.12 nm. The average pore widths of KOH-activated samples were strongly governed by the activation temperature. We expect that these approaches can be utilized to simply control the porosity of PVDC-derived nanoporous carbons.참고 자료
없음"Carbon Letters"의 다른 논문
Fabrication and Characterization of Porous Non-Woven Ca..6페이지
Dielectrophoretic Alignment and Pearl Chain Formation o..6페이지
Improved Electrical Conductivity of a Carbon Nanotube M..5페이지
Synthesis and Properties of Polyimide Composites Contai..6페이지
Vertically Aligned Carbon Film Synthesized from Magneti..4페이지