Effects of carbonization temperature on pore development in polyacrylonitrile-based activated carbon nanofibers
* 본 문서는 배포용으로 복사 및 편집이 불가합니다.
서지정보
ㆍ발행기관 : 한국탄소학회
ㆍ수록지정보 : Carbon Letters / 15권 / 2호
ㆍ저자명 : Hye-Min Lee, Kay-Hyeok An, Byung-Joo Kim
ㆍ저자명 : Hye-Min Lee, Kay-Hyeok An, Byung-Joo Kim
목차
1. Introduction2. Experiment Details
3. Results and Discussion
4. Conclusions
Acknowledgments
References
한국어 초록
In this work, activated carbon nanofiber (ACNF) electrodes with high double-layer capacitance and good rate capability were prepared from polyacrylonitrile nanofibers by optimizing the carbonization temperature prior to H2O activation. The morphology of the ACNFs was observed by scanning electron microscopy. The elemental composition was determined by analysis of X-ray photoelectron spectroscopy. N2-adsorption-isotherm characteristics at 77 K were confirmed by Brunauer-Emmett-Teller and Dubinin-Radushkevich equations. ACNFs processed at different carbonization temperatures were applied as electrodes for electrical double-layer capacitors. The experimental results showed that the surface morphology of the CNFs was not significantly changed after the carbonization process, although their diameters gradually decreased with increasing carbonization temperature. It was found that the carbon content in the CNFs could easily be tailored by controlling the carbonization temperature. The specific capacitance of the prepared ACNFs was enhanced by increasing the carbonization temperature.영어 초록
In this work, activated carbon nanofiber (ACNF) electrodes with high double-layer capacitance and good rate capability were prepared from polyacrylonitrile nanofibers by optimizing the carbonization temperature prior to H2O activation. The morphology of the ACNFs was observed by scanning electron microscopy. The elemental composition was determined by analysis of X-ray photoelectron spectroscopy. N2-adsorption-isotherm characteristics at 77 K were confirmed by Brunauer-Emmett-Teller and Dubinin-Radushkevich equations. ACNFs processed at different carbonization temperatures were applied as electrodes for electrical double-layer capacitors. The experimental results showed that the surface morphology of the CNFs was not significantly changed after the carbonization process, although their diameters gradually decreased with increasing carbonization temperature. It was found that the carbon content in the CNFs could easily be tailored by controlling the carbonization temperature. The specific capacitance of the prepared ACNFs was enhanced by increasing the carbonization temperature.참고 자료
없음"Carbon Letters"의 다른 논문
Fabrication of isotropic bulk graphite using artificial..4페이지
Facile preparation of self-assembled wool-based graphen..6페이지
Preparation of pitch from pyrolized fuel oil by electro..7페이지
Effect of stacking sequence on the flexural and fractur..4페이지
Study on lowering the percolation threshold of carbon n..8페이지
Study on electrochemical performances of sulfur-contain..4페이지
Removal of methylene blue using lemon grass ash as an a..8페이지
Superhydrophobic carbon-based materials: a review of sy..16페이지
Double-walled carbon nanotubes: synthesis, structural c..12페이지
My life and Korean carbon society4페이지