The effects of stacking sequence on the penetration-resistant behaviors of T800 carbon fiber composite plates under low-velocity impact loading
* 본 문서는 배포용으로 복사 및 편집이 불가합니다.
서지정보
ㆍ발행기관 : 한국탄소학회
ㆍ수록지정보 : Carbon Letters / 16권 / 2호
ㆍ저자명 : Furqan Ahmad, Jung-Wuk Hong, Heung Soap Choi, Soo-Jin Park, Myung Kyun Park
ㆍ저자명 : Furqan Ahmad, Jung-Wuk Hong, Heung Soap Choi, Soo-Jin Park, Myung Kyun Park
목차
1. Introduction2. Experimentation
3. Results and Discussion
4. Conclusions
References
한국어 초록
Impact damages induced by a low-velocity impact load on carbon fiber reinforced polymer(CFRP) composite plates fabricated with various stacking sequences were studied experimentally.The impact responses of the CFRP composite plates were significantly affected by thelaminate stacking sequences. Three types of specimens, specifically quasi-isotropic, unidirectional,and cross-ply, were tested by a constant impact carrying the same impact energy level.An impact load of 3.44 kg, corresponding to 23.62 J, was applied to the center of each platesupported at the boundaries. The unidirectional composite plate showed the worst impact resistanceand broke completely into two parts; this was followed by the quasi-isotropic lay-upplate that was perforated by the impact. The cross-ply composite plate exhibited the best resistanceto the low-velocity impact load; in this case, the impactor bounced back. Impact parameterssuch as the peak impact force and absorbed energy were evaluated and compared forthe impact resistant characterization of the composites made by different stacking sequences.영어 초록
Impact damages induced by a low-velocity impact load on carbon fiber reinforced polymer(CFRP) composite plates fabricated with various stacking sequences were studied experimentally.
The impact responses of the CFRP composite plates were significantly affected by the
laminate stacking sequences. Three types of specimens, specifically quasi-isotropic, unidirectional,
and cross-ply, were tested by a constant impact carrying the same impact energy level.
An impact load of 3.44 kg, corresponding to 23.62 J, was applied to the center of each plate
supported at the boundaries. The unidirectional composite plate showed the worst impact resistance
and broke completely into two parts; this was followed by the quasi-isotropic lay-up
plate that was perforated by the impact. The cross-ply composite plate exhibited the best resistance
to the low-velocity impact load; in this case, the impactor bounced back. Impact parameters
such as the peak impact force and absorbed energy were evaluated and compared for
the impact resistant characterization of the composites made by different stacking sequences.
참고 자료
없음태그
"Carbon Letters"의 다른 논문
Changes in the porosity of bulk graphite according to t..3페이지
Hydrogen storage capacity of highly porous carbons synt..5페이지
Stabilization of pitch-based carbon fibers accompanying..6페이지
Mechanisms of Na adsorption on graphene and graphene ox..5페이지
Functionalization of graphene nanoplatelets using sugar..6페이지