Changes in the porosity of bulk graphite according to the viscosity of resin for impregnation
* 본 문서는 배포용으로 복사 및 편집이 불가합니다.
서지정보
ㆍ발행기관 : 한국탄소학회
ㆍ수록지정보 : Carbon Letters / 16권 / 2호
ㆍ저자명 : Sang-Min Lee, Dong-Su Kang, Hye-Sung Kim, Jea-Seung Roh
ㆍ저자명 : Sang-Min Lee, Dong-Su Kang, Hye-Sung Kim, Jea-Seung Roh
목차
1. Introduction2. Experimental Procedure
3. Results and Discussion
4. Conclusions
References
한국어 초록
When manufacturing bulk graphite, pores develop within the bulk during the carbonization process due to the volatile components of the fillers and the binders. As a result, the physical properties of bulk graphite are inferior to the theoretical values. Impregnants are impregnated into the pores generated in the carbonization process through pressurization and/or depressurization. The physical properties of bulk graphite that has undergone impregnation and re-carbonization processes are outstanding. In the present study, a green body was manufactured by molding with natural graphite flakes and phenolic resin at 45 MPa. Bulk graphite was manufactured by carbonizing the green body at 700 and it was subsequently impregnated with impregnants having viscosity of 25.0 cP, 10.3 cP, and 5.1 cP, and the samples were re-carbonized at 700°C. The above process was repeated three times. The open porosity of bulk graphite after the final process was 22.25%, 19.86%, and 18.58% in the cases of using the impregnant with viscosity of 25.0 cP, 10.3 cP, and 5.1 cP, respectively.영어 초록
When manufacturing bulk graphite, pores develop within the bulk during the carbonization process due to the volatile components of the fillers and the binders. As a result, the physical properties of bulk graphite are inferior to the theoretical values. Impregnants are impregnated into the pores generated in the carbonization process through pressurization and/or depressurization. The physical properties of bulk graphite that has undergone impregnation and re-carbonization processes are outstanding. In the present study, a green body was manufactured by molding with natural graphite flakes and phenolic resin at 45 MPa. Bulk graphite was manufactured by carbonizing the green body at 700 and it was subsequently impregnated with impregnants having viscosity of 25.0 cP, 10.3 cP, and 5.1 cP, and the samples were re-carbonized at 700°C. The above process was repeated three times. The open porosity of bulk graphite after the final process was 22.25%, 19.86%, and 18.58% in the cases of using the impregnant with viscosity of 25.0 cP, 10.3 cP, and 5.1 cP, respectively.참고 자료
없음"Carbon Letters"의 다른 논문
Hydrogen storage capacity of highly porous carbons synt..5페이지
Stabilization of pitch-based carbon fibers accompanying..6페이지
Mechanisms of Na adsorption on graphene and graphene ox..5페이지
The effects of stacking sequence on the penetration-res..9페이지
Functionalization of graphene nanoplatelets using sugar..6페이지