1,2-Bis(4-trimellitimidophenoxy)benzene으로 부터 유도된 신규 방향족 폴리아미드이미드
(주)코리아스칼라
- 최초 등록일
- 2016.04.02
- 최종 저작일
- 2010.06
- 8페이지/
어도비 PDF
- 가격 4,000원
![할인쿠폰받기](/images/v4/document/ico_det_coupon.gif)
* 본 문서는 배포용으로 복사 및 편집이 불가합니다.
서지정보
ㆍ발행기관 : 한국유화학회
ㆍ수록지정보 : 韓國油化學會誌 / 27권 / 2호
ㆍ저자명 : 정화진
영어 초록
A series of noble poly(amide-imide)s and copoly(amide-imide)s bearing 1,2-bis(4-phenoxy)benzene units were synthesized by the direct polycondensation of 1,2-bis(4-trimellitimidophenoxy)benzene[1,2-PTPB] with a combination of commercially available aromatic diamines and diacids such as m-phenylene diamine, p-phenylene diamine(PPD), isophthalic acid and terephthalic acid(TA) in N-methyl-2-pyrrolidone(NMP) using triphenyl phosphite and pyridine as a condensing agent in the presence of dehydrating agent (CaCl2). The resulting polymers had inherent viscosities in the range of 0.37~0.78 dL/g and most of them were soluble m common organic solvents including NMP, dimethylacetamide, dimethylsulfoxide, dimethylformamide, and m-cresol. Wide-angle X-ray diffractograms revealed that the copoly(amide-imide) derived from PPD with mixed acids of 1,2-BTPB and TA, showed crystalline nature, whereas all of the other polymers were found to be amorphous. The glass transition temperatures of the polymers occurred over the temperature range of 270~323℃ in their differential scanning calorimetry curves and their 10% weight loss temperature, determined by thermogravimetric analysis in air and nitrogen atmosphere, were in the range 465~535℃, 500~550℃, respectively, indicating their good thermal stability.
참고 자료
없음
"韓國油化學會誌"의 다른 논문
더보기 (5/10)