지방산과 인지질 혼합 LB막의 전기화학적 특성
* 본 문서는 배포용으로 복사 및 편집이 불가합니다.
서지정보
ㆍ발행기관 : 한국유화학회
ㆍ수록지정보 : 韓國油化學會誌 / 20권 / 2호
ㆍ저자명 : 손태철, 김남석, 박근호
ㆍ저자명 : 손태철, 김남석, 박근호
영어 초록
We studied electrochemical characteristics of Langmuir-Blodgett(LB) films by using cyclic voltammetry with a three-electrode system. An Ag/AgCl as a reference electrode, a platinum wire as a counter electrode and LB film-coated indium tin oxide(ITO) as a working electrode were used to study electrochemical characteristics at a various concentration of NaClO4 solution. LB films were reduced from initial potential to -1350 mV, continuously oxidized to l650mV and returned to the initial point. The scan rate was l00mV/s. The monolayer surface morphology of the LB film have been measured by Atomic Force Microscope(AFM). As a result, We comfirmed that the microscopic properties of LB film by AFM showed the good orientation of momolayer molecules and the thickness of monolayer was 3.5-4.lnm. The cyclic voltammograms(CV) of the ITO-coated glass showed the peak potentials for the reduction-oxidation reation. LB films of 4-octyl-4'-(5-carboxypentamethyleneoxy) azobenzene(8A5H) / L-α-phosphayidyl choline, dilauroyl(DLPC) seemed to be irreversible process caused by only the oxidation current from the cyclic voltammogram. The current of oxidatation increased at cyclic voltammogram by increasing 8A5H density in LB films. The diffusivity(D) of LB films increased with increasing of a 8A5H amount and was inversely proportional to the concentration of NaClO4 solution.참고 자료
없음"韓國油化學會誌"의 다른 논문
HL에 의한 프로비타민-B5 액정의 형성과 보습효과9페이지
반응형 인계 난연도료의 제조 II. 폴리우레탄 도료의 제조 및 도막특성7페이지
탈지조성에 따른 철강용 알칼리탈지제의 합성 및 특성6페이지
Cyclovoltametric Methods for the Ionization Potential a..5페이지
마이크로에멀젼을 이용한 은 나노입자의 합성7페이지
Nano Clay를 이용한 난연성 Polyolefin Compound의 제조 및 특성에 관한 연구8페이지
Facilitated Transport of Cr(VI) through a Supported Liq..11페이지
Eicosanoic Acid Langmuir-Blodgett(LB) 박막을 이용한 분자 다이오드의 ..6페이지
공정변수를 조절한 폴리에틸렌 산화왁스 합성에 관한 연구7페이지
양친매성 스쿠아릴리움색소 초박막의 전기적 특성5페이지