마그네트론 코스퍼터링법으로 형성한 SiO2/Si 양자점 초격자 구조의 특성
* 본 문서는 배포용으로 복사 및 편집이 불가합니다.
서지정보
ㆍ발행기관 : 한국재료학회
ㆍ수록지정보 : 한국재료학회지 / 20권 / 11호
ㆍ저자명 : 박영빈, 김신호, 하린, 이현주, 이정철, 배종성, 김양도
ㆍ저자명 : 박영빈, 김신호, 하린, 이현주, 이정철, 배종성, 김양도
영어 초록
Solar cells have been more intensely studied as part of the effort to find alternatives to fossil fuels as power sources.The progression of the first two generations of solar cells has seen a sacrifice of higher efficiency for more economic use ofmaterials. The use of a single junction makes both these types of cells lose power in two major ways: by the non-absorptionof incident light of energy below the band gap; and by the dissipation by heat loss of light energy in excess of the band gap.Therefore, multi junction solar cells have been proposed as a solution to this problem. However, the 1st and 2nd generation solarcells have efficiency limits because a photon makes just one electron-hole pair. Fabrication of all-silicon tandem cells using anSi quantum dot superlattice structure (QD SLS) is one possible suggestion. In this study, an SiOx matrix system was investigatedand analyzed for potential use as an all-silicon multi-junction solar cell. Si quantum dots with a super lattice structure (Si QDSLS) were prepared by alternating deposition of Si rich oxide (SRO; SiOx (x=0.8, 1.12)) and SiO2 layers using RF magnetronco-sputtering and subsequent annealing at temperatures between 800 and 1,100oC under nitrogen ambient. Annealing temperaturesand times affected the formation of Si QDs in the SRO film. Fourier transform infrared spectroscopy (FTIR) spectra and x-rayphotoelectron spectroscopy (XPS) revealed that nanocrystalline Si QDs started to precipitate after annealing at 1,100oC for onehour. Transmission electron microscopy (TEM) images clearly showed SRO/SiO2 SLS and Si QDs formation in each 4, 6, and8nm SRO layer after annealing at 1,100oC for two hours. The systematic investigation of precipitation behavior of Si QDsin SiO2 matrices is presented.참고 자료
없음"한국재료학회지"의 다른 논문
산화아연-단일벽탄소나노튜브복합체의 일산화질소 감지 특성5페이지
태양전지용 실리콘 기판의 절삭손상 식각 조건에 의한 곡강도 변화6페이지
PAD법으로 제작된 산화코발트-산화주석 복합체의 가스 감응 특성6페이지
RF 마그네트론 코스퍼터링을 이용한 Si3N4 매트릭스 내부의 실리콘 양자점 제조연구5페이지
SiOC(-H) 박막 제조용 Methyltriphenylsilane 전구체 합성 및 특성분석6페이지
리튬 이차 전지를 위한 다공성 니켈-주석 나노 수지상 전극8페이지
수소주입에 따른 590 MPa급 DP강 표면층의 미소경도와 조직특성5페이지
Na2Ti6O13를 도핑한 0.94BaTiO3-0.06(Bi0.5Na0.5)TiO3 세라믹스의 미세..6페이지
지르코니아 광페룰 사출성형용 WC 코아 핀의 Diamond Like Carbon 코팅5페이지
Spark Plasma Sintering and Ultra-Precision Machining Ch..11페이지