이중 전기방사법을 이용하여 SnO2-Sn-Ag3Sn 나노 입자가 균일하게 내재된 탄소 나노섬유의 합성
* 본 문서는 배포용으로 복사 및 편집이 불가합니다.
서지정보
ㆍ발행기관 : 한국재료학회
ㆍ수록지정보 : 한국재료학회지 / 23권 / 2호
ㆍ저자명 : 안건형, 안효진
ㆍ저자명 : 안건형, 안효진
영어 초록
Well-distributed SnO2-Sn-Ag3Sn nanoparticles embedded in carbon nanofibers were fabricated using a co-electrospinning method, which is set up with two coaxial capillaries. Their formation mechanisms were successfully demonstrated. The structural, morphological, and chemical compositional properties were investigated by field-emission scanning electron spectroscopy (FESEM), bright-field transmission electron microscopy (TEM), X-ray diffraction (XRD), and X-ray photoelectron spectroscopy (XPS). In particular, to obtain well-distributed SnO2 and Sn and Ag3Sn nanoparticles in carbon nanofibers, the relative molar ratios of the Ag precursor to the Sn precursor including 7 wt% polyacrylonitrile (PAN) were controlled at 0.1, 0.2, and 0.3. The FESEM, bright-field TEM, XRD, and XPS results show that the nanoparticles consisting of SnO2-Sn-Ag3Sn phases were in the range of ~4 nm-6 nm for sample A, ~5 nm-15 nm for sample B, ~9 nm-22 nm for sample C. In particular, for sample A, the nanoparticles were uniformly grown in the carbon nanofibers. Furthermore, when the amount of the Ag precursor and the Sn precursor was increased, the inorganic nanofibers consisting of the SnO2-Sn-Ag3Sn nanoparticles were formed due to the decreased amount of the carbon nanofibers. Thus, well-distributed nanoparticles embedded in the carbon nanofibers were successfully synthesized at the optimum molar ratio (0.1) of the Ag precursor to the Sn precursor after calcination of 800˚C.참고 자료
없음"한국재료학회지"의 다른 논문
Detection of Delamination Crack for Polymer Matrix Comp..5페이지
스파크플라즈마 소결에 의한 Ti-Nb-Zr-Mo-CPP 생체복합재의 기계적 성질 및 생체적합성8페이지
LiCl-Li2O 용융염에서 Inconel 합금 및 Incoloy 800H의 고온 부식거동7페이지
산화성 고온 리튬용융염계 분위기에서 Pyro-Carbon의 부식거동5페이지
실리콘 기판 표면 형상에 따른 반사특성 및 광 전류 개선 효과7페이지
New Surface Treatment Process in Magnesium Alloy for Wh..4페이지
GaOOH로부터 GaN 분말의 합성에 미치는 B2O3의 첨가효과8페이지
기계적 합금법으로 제조한 Mg3-xZnxSb2의 열전물성6페이지
초고속 유성형 매체 분쇄기를 이용한 건식분쇄공정에서 Al/CNTs 복합재 제조를 위한 알루미늄분말의..9페이지
Infleunce of Nozzle Tip Size on the Preparation of Nano..8페이지