리튬 이차전지용 텅스텐 산화물 전해 도금 박막 제조
* 본 문서는 배포용으로 복사 및 편집이 불가합니다.
서지정보
ㆍ발행기관 : 한국재료학회
ㆍ수록지정보 : 한국재료학회지 / 23권 / 12호
ㆍ저자명 : 이준우, 최우성, 신헌철
ㆍ저자명 : 이준우, 최우성, 신헌철
영어 초록
Tungsten oxide films were prepared by an electrochemical deposition method for use as the anode in rechargeable lithium batteries. Continuous potentiostatic deposition of the film led to numerous cracks of the deposits while pulsed deposition significantly suppressed crack generation and film delamination. In particular, a crack-free dense tungsten oxide film with a thickness of ca. 210 nm was successfully created by pulsed deposition. The thickness of tungsten oxide was linearly proportional to deposition time. Compositional and structural analyses revealed that the as-prepared deposit was amorphous tungsten oxide and the heat treatment transformed it into crystalline triclinic tungsten oxide. Both the as-prepared and heat-treated samples reacted reversibly with lithium as the anode for rechargeable lithium batteries. Typical peaks for the conversion processes of tungsten oxides were observed in cyclic voltammograms, and the reversibility of the heat-treated sample exceeded that of the as-prepared one. Consistently, the cycling stability of the heat-treated sample proved to be much better than that of the as-prepared one in a galvanostatic charge/discharge experiment. These results demonstrate the feasibility of using electrolytic tungsten oxide films as the anode in rechargeable lithium batteries. However, further works are still needed to make a dense film with higher thickness and improved cycling stability for its practical use.참고 자료
없음"한국재료학회지"의 다른 논문
중국의 재료과학분야 연구현황과 우리의 대응방안12페이지
열처리를 통한 금 나노입자의 크기 제어와 일벽 탄소나노튜브의 합성 촉매로의 이용8페이지
HVPE법에 의해 성장된 AlN 에피층의 V/III비에 따른 특성변화5페이지
고상법에 의한 BaSrSiO4 형광체의 분말합성 및 발광특성5페이지
금속산화물 복합분말의 동결건조 및 수소분위기 환원처리에 의한 Cu-Sn 다공체 제조5페이지
Hot Wall Epitaxy(HWE)법에 의한 ZnAl2Se4 단결정 박막 성장과 가전자대 갈라짐..8페이지
마이크로파 조사가 산화그래핀의 화학적 박리에 미치는 효과6페이지
Protective SiC Coating on Carbon Fibers by Low Pressure..6페이지
강화상 나노입자의 용액 반응성이 구리 도금 박막에 미치는 영향7페이지
CSA를 사용한 플라이애시 콘크리트의 초기강도 개선을 위한 실험연구8페이지