아스팔트 콘크리트 포장용 균열실링재의 부착특성 평가
* 본 문서는 배포용으로 복사 및 편집이 불가합니다.
서지정보
ㆍ발행기관 : 한국도로학회
ㆍ수록지정보 : 한국도로학회논문집 / 17권 / 2호
ㆍ저자명 : 이재준, 김승훈, 백종은, 임재규, 김용주
ㆍ저자명 : 이재준, 김승훈, 백종은, 임재규, 김용주
영어 초록
Cracking is an inevitable fact of asphalt concrete pavements and plays a major role in pavement deterioration. Pavement cracking is one of the main factors determining the frequency and method of repair. Cracks can be treated with a number of preventative maintenance actions, including overlay surface treatments such as slurry sealing, crack sealing, or crack filling. Pavement cracks can show up as one or all of the following types: transverse, longitudinal, fatigue, block, reflective, edge, and slippage. Crack sealing is a frequently used pavement maintenance treatment because it significantly extends the pavement service life. However, crack sealant often fails prematurely due to a loss of adhesion. Because current test methods are mostly empirical and only provide a qualitative measure of the bond strength, they cannot accurately predict the adhesive failure of the sealant. This study introduces a laboratory test aimed at assessing the bonding of hot-poured crack sealant to the walls of pavement cracks. A pneumatic adhesion tensile testing instrument (PATTI) was adopted to measure the bonding strength of the hot-poured crack sealant as a function of the curing time and temperature. Based on a limited number of test results, the hot-poured crack sealants have very different bonding performances. Therefore, this test method can be proposed as part of a newly developed performancebased standard specification for hot-poured crack sealants for use in the future.PURPOSES : The purpose of this study was to evaluate both the adhesion and failure performance of a crack sealant as a function of its curing time and curing temperature.
METHODS: A pneumatic adhesion tensile testing instrument (PATTI) was adopted to measure the adhesion performance of a crack sealant as a function of the curing time and curing temperature.
RESULTS: With changes in the curing time, curing temperature, and sealant type, the bond strengths were found to be significantly different. Also, higher bond strengths were measured at lower temperatures. Different sealant types produced completely different bond strengths and failure behaviors.
CONCLUSIONS: The bonding strength of an evaluated crack sealant was shown to differ depending on various factors. Two sealant types, which were composed of different raw materials, were shown to perform differently. The newly proposed test offers the possibility of evaluating anddifferentiatingbetweendifferentcracksealants.Basedonalimitednumberoftestresults,this test method can be proposed as part of a newly developed performance-based standard specification for crack sealants or as part of a guideline for the selection of hot-poured crack sealant in the future.
참고 자료
없음"한국도로학회논문집"의 다른 논문
도로 종류와 도로생애주기별 탄소배출량, 에너지소모량 및 비용에 대한 거시적 분석방법8페이지
주변 환경 순응형 자동차 경적 소음 개선 방법7페이지
다수단 Mode를 고려한 도시부 도로의 서비스수준 평가방법에 관한 기초연구12페이지
가상주행과 실차주행의 운전자 주행행태 차이에 관한 연구16페이지
알칼리 활성화된 고로슬래그 페이스트의 물리화학적 특성 및 이산화탄소 흡수능 평가7페이지
아스팔트 도로포장 유지보수용 표면처리공법의 공용성 평가10페이지
겨울철 도시부 노면결빙사고 발생에 미치는 요소에 관한 연구9페이지
마이크로서페이싱의 성공과 실패 사례8페이지
도로유실 복구를 위한 골재 충전 고흐름도 모르타르의 기초 배합 연구8페이지
광물질혼화재를 적용한 콘크리트의 스케일링 저항성 평가7페이지