Microstructure and Characterization of Ni-C Films Fabricated by Dual-Source Deposition System
(주)코리아스칼라
- 최초 등록일
- 2016.08.09
- 최종 저작일
- 2016.06
- 5페이지/ 어도비 PDF
- 가격 4,000원
* 본 문서는 배포용으로 복사 및 편집이 불가합니다.
서지정보
ㆍ발행기관 : 한국재료학회
ㆍ수록지정보 : 한국재료학회지 / 26권 / 6호
ㆍ저자명 : Chang-Suk Han, Sang-Wook Kim
목차
1. Introduction
2. Experimental Procedure
3. Results and Discussion
3.1 Microstructures of Ni-C films
3.2 Electrical properties of Ni-C films
4. Conclusions
Acknowledgements
References
영어 초록
Ni-C composite films were prepared by co-deposition using a combined technique of plasma CVD and ion beam sputtering deposition. Depending on the deposition conditions, Ni-C thin films manifested three kinds of microstructure: (1) nanocrystallites of non-equilibrium carbide of nickel, (2) amorphous Ni-C film, and (3) granular Ni-C film. The electrical resistivity was also found to vary from about 102 μΩcm for the carbide films to about 104 μΩcm for the amorphous Ni-C films. The Ni-C films deposited at ambient temperatures showed very low TCR values compared with that of metallic nickel film, and all the films showed ohmic characterization, even those in the amorphous state with very high resistivity. The TCR value decreased slightly with increasing of the flow rate of CH4. For the films deposited at 200 oC, TCR decreased with increasing CH4 flow rate; especially, it changed sign from positive to negative at a CH4 flow rate of 0.35 sccm. By increasing the CH4 flow rate, the amorphous component in the film increased; thus, the portion of Ni3C grains separated from each other became larger, and the contribution to electrical conductivity due to thermally activated tunneling became dominant. This also accounts for the sign change of TCR when the filme was deposited at higher flow rate of CH4. The microstructures of the Ni-C films deposited in these ways range from amorphous Ni-C alloy to granular structures with Ni3C nanocrystallites. These films are characterized by high resistivity and low TCR values; the electrical properties can be adjusted over a wide range by controlling the microstructures and compositions of the films.