Relationships between dielectric properties and characteristics of impregnated and activated samples of potassium carbonateand sodium hydroxide-modified palm kernel shell for microwave- assisted activ

서지정보

ㆍ발행기관 : 한국탄소학회 ㆍ수록지정보 : Carbon letters / 24권
ㆍ저자명 : Norulaina Alias, Muhammad Abbas Ahmad Zaini, Mohd Johari Kamaruddin

목차

Abstract
1. Introduction
2. Experimental
3. Results and Discussion
3.1. Characteristics of samples
3.2. Frequency-dependency of the dielectricproperties
3.3. Temperature-dependency of the dielectricproperties
3.4. Relaxation time and penetration depthof the PKS-modified samples
3.5. Correlations between the dielectric propertiesand material characteristics
4. Conclusions
Conflict of Interest
Acknowledgements
References

영어 초록

The aim of this work was to evaluate the dielectric properties of impregnated and activated palm kernel shells (PKSs) samples using two activating agents, potassium carbonate (K2CO3) and sodium hydroxide (NaOH), at three impregnation ratios. The materials were characterized by moisture content, carbon content, ash content, thermal profile and functional groups. The dielectric properties were examined using an open-ended coaxial probe method at various microwave frequencies (1–6 GHz) and temperatures (25, 35, and 45°C). The results show that the dielectric properties varied with frequency, temperature, moisture content, carbon content and mass ratio of the ionic solids. PKSK1.75 (PKS impregnated with K2CO3 at a mass ratio of 1.75) and PKSN1.5 (PKS impregnated with NaOH at a mass ratio of 1.5) exhibited a high loss tangent (tan δ) indicating the effectiveness of these materials to be heated by microwaves. K2CO3 and NaOH can act as a microwave absorber to enhance the efficiency of microwave heating for low loss PKSs. Materials with a high moisture content exhibit a high loss tangent but low penetration depth. The interplay of multiple operating frequencies is suggested to promote better microwave heating by considering the changes in the materials characteristics.

참고 자료

없음