Photoelectrochemical and electrochemical urea oxidation with microwave‑assisted synthesized Co‑Fe2O3@NiO core–shell nanocomposites
* 본 문서는 배포용으로 복사 및 편집이 불가합니다.
서지정보
ㆍ발행기관 : 한국탄소학회
ㆍ수록지정보 : Carbon letters / 32권 / 4호
ㆍ저자명 : Assia Karrab, Remi Bensimon, Diane Muller, Stéphane Bastide, Christine Cachet‑Vivier, Salah Ammar
ㆍ저자명 : Assia Karrab, Remi Bensimon, Diane Muller, Stéphane Bastide, Christine Cachet‑Vivier, Salah Ammar
목차
Abstract1 Introduction
2 Experimental
2.1 Materials
2.2 Synthesis of pure, Co-doped α-Fe2O3 and Co-Fe2O3@NiO nanoparticles
2.3 Preparation of α-Fe2O3, Co-Fe2O3 and Co-Fe2O3@NiO nanoparticles modified GC electrode
2.4 Preparation of the α-Fe2O3, Co-Fe2O3 and Co-Fe2O3NiO films
2.5 Characterization
2.6 Electrochemical and photoelectrochemical measurements
3 Result and discussion
3.1 Structural analysis
3.2 SEM observationsEDX
3.3 Fourier Transform Infra-Red (FT-IR) spectroscopy
3.4 Optical analysis
3.5 Electrochemical measurement
3.6 Electrocatalytic oxidation of urea
3.7 Photoelectrochemical measurement
4 Conclusion
Acknowledgements
References
영어 초록
This work reported the electrochemical and photoelectrochemical (PEC) properties of a new photoelectrode based on hematite Co-Fe2O3@NiO, a photoactive semiconductor, was prepared using a process involving a combination of the co-precipitation and microwave-assisted synthesis of Fe2O3, Co-Fe2O3 and Co-Fe2O3@NiO, respectively. The obtained products were characterized by X-Ray powder Diffraction (XRD), Scanning Electron Microscope (SEM), Energy Dispersive X-ray analysis (EDX), Ultraviolet–Visible (UV–vis) analysis, Fourier Transform Infrared spectroscopy (FT-IR). X-ray diffraction (XRD) pattern of the sample determined the crystal structure of α-Fe2O3 nanoparticles. The SEM image shows spherical nanoparticles. FTIR spectrospy spectrum confirmed the phase purity and chemical bond for the sample. Optical studies show a variation of band gap from 2.118 to 2.07 eV. The electrochemical and photoelectrochemical (PEC) performance of the films were examined by cyclic voltammetry, linear sweep voltammetry and chronoamperometry. The electrochemical oxidation of water achieved by Cobalt-doped Fe2O3@ GCE modified electrode exhibited the current density of 21 mA/g at 0.5 V vs. SCE for 5 at% of Co and reveals enhanced specific capacitance of 352.11 F/g. The catalytic performance of urea oxidation was measured by cyclic voltammetry on Co-Fe2O3@NiO nanoparticles modified glassy carbon electrode (GCE) in alkaline medium. The electrode Co-Fe2O3@NiO without annealing showed a peak current density of 1.59 mA/cm2 at 0.1 M urea in 1.0 M NaOH, which was 3.6 fold higher than that of Co-Fe2O3@NiO with annealing. In another part, this work reported the photoelectrochemical (PEC) properties of photoanode prepared by spin coating. The highest photocurrent 0.042 mA/cm2 at 0.5 V Vs SCE was obtained for 5% Co-Fe2O3@NiO while the photocatalytic oxidation of urea.참고 자료
없음"Carbon letters"의 다른 논문
Realization of diamond nucleation within the multi‑wall..12페이지
Fibrous and granular activated carbon mixed media for e..8페이지
The relationship between the molecular composition of c..9페이지
Assessment of carbon fibers recovered from lab‑scale ve..15페이지
In situ synthesis NiO/F‑MWCNTs nanocomposite for adsorp..12페이지
Development of nitrogen‑decorated carbon dots (NCDs) th..8페이지
Reusable, magnetic laser‑induced graphene for efficient..18페이지
Facile scalable synthesis of graphene oxide and reduced..16페이지
Electrocatalytic reduction of 2,4 dinitrophenol on carb..13페이지
Influence of carbon nanotube inclusions to electrical, ..12페이지