Development of high-efficiency flexible Cu(In,Ga)Se2 solar cells: A study of
alkali doping effects on CIS, CIGS, and CGS using alkali-silicate glass thin layers
Shogo Ishizuka *, Akimasa Yamada, Koji Matsubara, Paul Fons, Keiichiro Sakurai, Shigeru Niki
deposition 증착 flexible zirconia sheet substrates silicate 규산염
Development of high-efficiency flexible Cu(In,Ga)Se2 solar cells: A study of
alkali doping effects on CIS, CIGS, and CGS using alkali-silicate glass thin layers
Shogo Ishizuka *, Akimasa Yamada, Koji Matsubara, Paul Fons, Keiichiro Sakurai, Shigeru Niki
<중 략>
4. Conclusions
CIS, CIGS and CGS solar cells were fabricated on flexible zirconia sheet substrates using SLGTF as alkali source material.
CIS, CIGS 그리고 CGS 태양전지는 알칼리 원재료처럼 SLGTF를 사용하여 구부릴 수 있는 지르코니아 시트 기질로 제작된다.
The grain size of the CIGS absorber layers decreased with the use of SLGTF, that is, with the presence of Na in CIGS regardless of the In/Ga composition ratio in CIGS.
CIGS 흡수층의 grain size는 SLGTF의 사용으로 감소한다. 이것은 CIGS안에서 In/Ga의 합성 비율에 상관없이 CIGS의 Na 함유량에 따라 나타난다.